Influence of the background, substrate and thickness in light behaviour and colour of zirconia-reinforced lithium silicate (ZLS) glass-ceramic / Influência do fundo, substrato e espessura no comportamento da luz e cor das cerâmicas de dissilicato de lítio reforçadas com zircónia (ZLS)

Objective: To evaluate the influence of background, substrates and thickness on the color and light behaviour of two ZLS glass ceramics. Material and Methods: Standardized disc-shape specimens (12 x 1.2 mm), color A1 HT, of Celtra Duo and Vita Suprinity (n=30), were tested over a white/black background, and divided in five groups (n=6) to be tested over five substrates (polished gold alloy, white zirconia and composite, dentine and enamel A1 colour). The L*, C*, h*, a*, b* and Δ E values, were recorded in two thicknesses (1.2 and 2.4 mm). Translucency parameter (TP), contrast ratio (CR) and opalescence parameter (OP) were calculated. Data was analysed with non­parametric tests: Mann Whitney between ceramic materials for thickness, Wilcoxon for thicknesses in substrates and ceramic material and Kruskal­Wallis with Bonferroni corrections tests (p<0,01) for substrates. Results: For 2.4 mm, the Δ E values were always higher independently of ceramic material or substrates. Vita Suprinity registered lower values than Celtra Duo. Zirconia substrate registered the lower values. For 1.2 mm, dentine registered the lower values. Gold alloy and composite substrates registered the lower Δ E values for 1.2 mm Celtra Duo and 2.4 mm Vita Suprinity specimens. CT and OP higher values and TP lower values were registered for 2.4 mm Vita Suprinity. It was impossible to calculate for Celtra Duo specimens. Conclusions: Background, substrate and thickness had significant influence in light behaviour and final color of ZLS glass ceramics. Substrates Gold alloy and dentine exhibited clinical acceptable Δ E values for 1.2 mm Celtra Duo specimens. (AU)

Objetivo: Avaliar a influência do fundo, do substrato e da espessura no comportamento da luz e na cor de duas cerâmicas ZLS. Material e métodos: Discos de cerâmica (12 x 1.2 mm) de cor A1 HT, de Celtra Duo e Suprinity (n=30), foram testados sobre fundo branco/preto e cinco substratos (liga Ag-Au-Pt polida; zircónia branca; compósito, dentina e esmalte de cor A1). Os valores L*, C*, h*, a*, b* e Δ E foram registados em duas espessuras (1.2 mm e 2.4 mm). O parâmetro de translucidez (TP), o parâmetro de opalescência (OP) e o índice de contraste (CR) foram determinados. Foram realizados testes não paramétricos: Mann Whitney entre cerâmicas por espessura, Wilcoxon entre categoria de espessura por substrato e cerâmica; Kruskal­Wallis com correção de Bonferroni para substratos (p <0,01). Resultados: Para 2,4 mm, o Δ E foi sempre superior independentemente do material ou substrato. Os valores de Suprinity foram inferiores aos de Celtra Duo. O substrato zirconia obteve o Δ E mais baixo. Para 1,2 mm, a dentina obteve o Δ E mais baixo. A liga dourada e o compósito obtiveram Δ E mais baixo para Celtra Duo 1,2 mm e Suprinity 2,4 mm. Para Suprinity, CT e OP foram maiores para 2,4 mm e menores para TP. Não foi possível calcular para Celtra Duo. Conclusão: O fundo, substrato e espessura tiveram influência significativa no comportamento da luz e cor das restaurações de cerâmica ZLS. Apenas os substratos metal e dentina apresentaram valores clinicamente aceitáveis, para Celtra Duo na espessura de 1.2 mm.(AU)

Trueness and precision of the reproduction of dental casts by the conventional, milling and 3D printing techniques / Fidelidade e precisão de modelos de trabalho reproduzidos pelas técnicas convencional, de fresagem e de impressão 3D

Objective: To compare the reproduction trueness and precision of dental casts made by the conventional, milling and 3D printing techniques. Material and Methods: From an upper right side half-arch reference model (RM), 72 models were obtained and divided into three groups: conventional (CM), milled (MM) and printed (PM). All models were scanned and converted into standard tessellation language (.STL) files. The files were superimposed using 3D analysis software, and statistical analysis was performed using the root mean square (RMS) values obtained. The Shapiro-Wilk test was used to assess normality, and the Kruskal-Wallis test was used to compare groups (ρ < ⍺; ⍺ = 0.05). The Mann-Whitney U test was used for multiple comparisons among groups (ρ < ਕ; ਕ = 0.017). Results: There were significant differences in trueness (ρ = 0.000; ρ <0.001) and precision (ρ = 0.000; ρ < 0.001) among the three dental cast groups. Regarding trueness, CM presented better results, followed by MM and PM. Regarding precision, MM showed better results, followed by PM and CM, which did not show significant differences. Conclusions: For dental cast reproduction the conventional technique has the best trueness and the milling technique has the best precision.(AU)

Objetivo: Comparar a fidelidade e precisão de reprodução de modelos de trabalho pelas técnicas convencional, de fresagem e de impressão 3D. Material e Métodos: A partir de um modelo de referência (MR) de uma hemi-arcada superior direita, foram obtidos 72 modelos divididos em três grupos: convencionais (MC), fresados (MF) e impressos (MI). Todos foram digitalizados e convertidos sob a forma de ficheiros .STL (standard tesselation language). Os ficheiros foram sobrepostos utilizando um software de análise 3D, e através dos valores RMS (raiz do valor quadrático médio) obtidos foi realizada a análise estatística. Para avaliação da normalidade foi utilizado o teste Shapiro Wilk e para a comparação entre grupos foi utilizado o teste Kruskal-Wallis (ρ < ⍺; ⍺ = 0.05). Para as comparações múltiplas entre grupos, foi utilizado o teste U de Mann-Whitney (ρ < ਕ; ਕ = 0.017). Resultados:Existem diferenças significativas de fidelidade (ρ = 0.000; ρ <0.001) e precisão (ρ = 0.000; ρ < 0.001) entre os três grupos. Em relação à fidelidade, MC apresentou melhores resultados, seguido por MF e MI. Em relação à precisão, MF apresentou melhores resultados, seguido por MI e MC, que não apresentaram diferenças significativas entre si. Conclusão: Para reprodução de modelos de trabalho, a técnica convencional é a que apresenta maior fidelidade e a técnica de fresagem a que apresenta maior precisão.(AU)

Evaluation of the influence of the impression technique, scanning direction and type of scanner on the accuracy of the final model / Avaliação da influência da técnica de impressão, direção de digitalização e tipo de scanner na precisão do modelo final

Objective: The purpose of this study is to evaluate the influence of the type of scanner and scanning direction on the accuracy of the final cast. Material and Methods: A partial master cast was used as a reference. A total of 128 scans were obtained and divided into two groups: the conventional method and the digital method. The digital group was divided into three groups: TRIOS 3, Omnicam and CS 3600. Each of these groups was subdivided according to the scanning direction, and each scan was overlaid on the digital reference cast to measure the trueness and precision of the procedures. Results: The overall precision values for the type of impression were 59.89 ± 13.08 µm for conventional and 13.42 ± 4.28 µm for digital; the values for trueness were 49.37 ± 19.13 µm for conventional and 53.53 ± 4.97 µm for digital; the scanning direction trueness values were 53.05 ± 4.36 µm for continuous and 54.03 ± 5.52 µm for segmented; and the precision values were 14.18 ± 4.67 µm for continuous and 12.67 ± 3.75 µm for segmented (p> 0.05). For the scanner type, the trueness values were 50.06 ± 2.65 µm for Trios 3, 57.45 ± 4.63 µm for Omnicam, and 52.57 ± 4.65 µm for Carestream; and those for precision were 11.7 ± 2.07 µm for Trios 3, 10.09 ± 2.24 µm for Omnicam, and 18.49 ± 2.42 µm for Carestream (p <0.05). Conclusions: The digital impression method is the most favorable method regarding precision; in terms of trueness, there are no differences between the types of impressions. (AU)

Objetivo: O objetivo deste estudo é avaliar a influência do tipo de técnica de moldagem, tipo de escâner intraoral e direção do escaneamento na precisão do modelo final. Material e Métodos: Um modelo parcial mestre foi usado como referência. Um total de 128 escaneamentos foi obtido e dividido em dois grupos: o método convencional (n = 32) e o método digital (n = 96). O grupo digital foi dividido em três grupos: TRIOS 3 (n = 32), Omnicam (n = 32) e CS 3600 (n = 32). Cada um desses grupos foi subdividido de acordo com a direção do escaneamento (n = 16), e cada escaneamento foi sobreposto ao modelo de referência digital para medir a veracidade e precisão dos procedimentos. Resultados: Os valores gerais de precisão para o tipo de impressão foram 59,89 ± 13,08 µm para convencional e 13,42 ± 4,28 µm para digital; os valores de veracidade foram 49,37 ± 19,13 µm para convencional e 53,53 ± 4,97 µm para digital; os valores de veracidade para a direção de digitalização foram 53,05 ± 4,36 µm para contínua e 54,03 ± 5,52 µm para segmentada; e os valores de precisão foram 14,18 ± 4,67 µm para contínua e 12,67 ± 3,75 µm para segmentada (p> 0,05). Para o tipo de scanner, os valores de veracidade foram 50,06 ± 2,65 µm para Trios 3, 57,45 ± 4,63 µm para Omnicam e 52,57 ± 4,65 µm para Carestream; e os de precisão foram 11,7 ± 2,07 µm para Trios 3, 10,09 ± 2,24 µm para Omnicam e 18,49 ± 2,42 µm para Carestream (p <0,05). Conclusões: O método de moldagem digital é o método mais favorável em relação à precisão; em termos de veracidade, não há diferenças entre os tipos de impressão (AU)

Biological Restorations: A foreseeable possibility in the junction between dentistry and technology / Restaurações Biológicas: Uma possibilidade previsível no encontro da Odontologia com a Tecnologia

Prosthetic rehabilitation can generate doubts among professionals regarding the type of material to choose when planning rehabilitation treatments. The establishment of reliable criteria for material selection raises frequent questions. This work presents a concept and an alternative and simplified proposal to paradigm shift in therapeutic approaches based on three trends in restorative dentistry: Biomimetics, the use of natural tissue as a restorative material, which offers potential for the recovery of the mechanical, aesthetic and biological properties of teeth; digital dentistry and CAD/CAM systems; and adhesive technology, which has undergone exponential and impressive advances. However, further studies are needed to evaluate the long-term performance of restorations in this variable field. (AU)

Muitas dúvidas surgem quanto ao tipo ideal de material restaurador a ser escolhido durante a elaboração do planejamento em tratamentos reabilitadores. Determinar critérios seguros para seleção do material são questionamentos frequentes. Este trabalho apresenta, por meio de um caso clínico, um conceito: restaurações biológicas e uma proposta alternativa e simplificada para quebrar paradigmas quanto a novas abordagens terapêuticas com as três tendências da Odontologia Restauradora Moderna: Biomimética ­ mimetizar e/ou utilizar o tecido natural dental como o material restaurador, com potencial de recuperar as propriedades mecânicas, estéticas e biológicas dos dentes danificados, a Odontologia digital e Sistemas CAD/CAM - com avanços exponenciais e a consagrada tecnologia adesiva. Porém mais estudos ainda são necessários para avaliar o desempenho a longo prazo dessas restaurações neste vasto campo de variabilidades. (AU)

Impact of crystallization firing process on the microstructure and flexural strength of zirconia-reinforced lithium silicate glass-ceramics.

OBJECTIVES: The aim of this study was to characterize the microstructure of two zirconia-reinforced lithium silicate (ZLS) glass-ceramics and evaluate their mechanical properties before and after the crystallization firing process (CFP). METHODS: Field emission-scanning electron microscope (FE-SEM) and energy-dispersive X-ray spectroscopy (EDS) analyses were performed for microstructural characterization. To evaluate the pattern of crystallization and the molecular composition of ZLS glass-ceramics, was used X-ray diffraction (XRD). Vickers hardness, fracture toughness by the indentation method, and biaxial flexural strength were also measured. One hundred and forty ceramic discs were produced (diameter=12mm; thickness=1.2mm) and allocated among four groups (n=30): Sfir, Sunf-ZLS Vita Suprinity; and Cfir and Cunf-ZLS Celtra Duo; fired and unfired, respectively. Statistical analysis was performed and Weibull failure probabilities were calculated. RESULTS: Cfir showed the highest characteristic strength (251.25MPa) and hardness (693.333±10.85GPa). Conversely, Sunf presented the lowest characteristic strength (106.95MPa) and significantly lowest hardness (597.533±33.97GPa). According to Weibull analysis, Sunf had the highest structural reliability (m=7.07), while Sfir presented the lowest (m=5.38). The CFP was necessary to crystallize zirconia in the partially crystallized ZLS glass-ceramics. Sfir had a lower percentage of crystallized zirconia than did Cfir. Fractographic analyses showed that all failures initiated from an inherent critical defect in Sunf and from processing defects in the remaining groups. SIGNIFICANCE: The CFP had a direct influence on the flexural strength and microstructural characteristics of both ZLS materials.

Cimentação adesiva dos retentores de fibra de vidro: o que precisamos saber? / Adhesive cementation of fiber posts: what we need to know?

Este artigo descreveu, através de uma revisão da literatura, conceitos atuais acerca da cimentação adesiva de pinos de fibra de vidro. Já que a união entre cimento resinoso, pino e dentina assume um papel importante na longevidade do tratamento protético restaurador. Na presente revisão, foram discutidos tópicos como a influência da espessura do cimento, as estratégias adesivas que podem ser utilizadas e fatores que podem influenciar na escolha do tipo de cimento resinoso a ser utilizado, os métodos indicados para a inserção desses cimentos no interior do conduto radicular e os conceitos referentes ao tratamento de superfície, tanto do pino de fibra como da superfície dentinária.

This paper has described through current literature concepts the adhesive cementation of fiberglass posts since the adhesive union between resin cement, post and dentin plays an important role in the longevity of the restorative and prosthetic treatment. The present review discussed topics such as: the influence of cement thickness, the adhesive strategies that can be used and factors that may influence the choice of the type of resin cement to be used, the methods indicated for the insertion of these cements inside the root canal, and concepts regarding the surface treatment of both post and dentin surfaces.